Tus nqi zoo (Qhov hnyav %)
| Nickel | 38.0 min.–46.0 max. | Hlau | 22.0 feeb. |
| Chromium | 19.5 min.–23.5 dr hab. | Molybdenum | 2.5 feeb - 3.5 max. |
| Molybdenum | 8. 0 min.-10 0 max. | Tooj | 1.5 feeb–3.0 max. |
| Titanium | 0.6 min.–1.2 max. | Cov pa roj carbon | 0.05 max. |
| Niobium (ntxiv rau Tantalum) | 3.15 feeb.-4.15 max. | Titanium | 0.40 |
| Cov pa roj carbon | 0.10 | Manganese | 1 00 max. |
| Sulfur | 0.03 max. | Silicon | 0.5 max. |
| Aluminium | 0.2 max. |
Mechanical Properties
Hom Chav Kub Kub Mechanical Properties, Mill Annealed
| Yield zog 0.2% Offset |
Qhov kawg Tensile Lub zog |
Elongation ua 2in. |
Hardness | ||
| psi (min.) | (MPa) | psi (min.) | (MPa) | % (min.) | Rockwell B |
| 49,000 | 338 | 96,000 | 662 | 45 | 135-165 |
| Kub, degree F | 70 | 400 | 600 | 800 | 1000 | 1200 | 1400 | 1600 |
| Qhov kawg Tensile Strength, ksi | 144 | 134 | 132 | 132 | 130 | 119 | 78 | 40 |
| 0.2% Yield Strength, ksi | 84 | 66 | 63 | 61 | 61 | 60 | 59 | 39 |
| Elongation,% | 44 | 45 | 42.5 | 45 | 48 | 34 | 59 | 117 |
Hom Rupture Strength Bar, Kev ntxhov siab rau Rupture ntawm lub sijhawm qhia
| Kub, degree F | 1200 | 1300 | 1400 |
| 100 h, ksi | 59 | 34 | 18 |
| 1,000 teev, ksi | 43 | 23 | 12 |
INCONEL thiab INCOLOY yog cov cim lag luam ntawm Cov Hlau Tshwj Xeeb (PCC)
Cim npe nrov: Tuam Tshoj alloy 825 daim hlau los yog alloy 825 npib tsib xee alloy phaj, Tuam Tshoj alloy 825 daim hlau los yog alloy 825 npib tsib xee alloy phaj manufacturers, lwm tus neeg, Hoobkas